Wear-resisting PC

Density

Shrinkage

Tensile Strength at break

Elongation at break

Flexural Modulus

Izod notched Impact Strength

HDT

Flame rating

Characteristic

Test Method
ASTM

g/cm3

%

MPa

%

MPa

J/m

℃（1.82MPa）

1.6mm

D792

D955

D638

D638

D790

D256

D648

UL94

C600PT1

1.24

0.4-0.7

58

30

2400

120

125

HB

5%PTFE reinforced, wear-resistant

C600PT2

1.26

0.4-0.7

55

10

2300

120

125

HB

10%PTFE reinforced, wear-resistant

C600PT3

1.28

0.4-0.7

55

10

2300

110

130

HB

15%PTFE reinforced, wear-resistant

C600PT4

1.32

0.4-0.7

50

7

2200

110

130

HB

20%PTFE reinforced, wear-resistant

C102PT4

1.39

0.3-0.5

90

6

3450

100

137

HB

10%GF,20%PTFE reinforced, wear-resistant

C162PT3

1.32

0.3-0.5

110

3

6500

110

140

HB

10%CT,15%PTFE reinforced, wear-resistant

C162PT4

1.34

0.3-0.5

105

3

6500

110

140

HB

10%CT,18%PTFE Reinforced, wear-resistant,scratch-resistant

C104PT3

1.43

0.2-0.3

90

3

5000

95

135

HB

20%GF,15%PTFE Reinforced, wear-resistant, scratch-resistant

C164PT3

1.36

0.2-0.3

120

2

9000

60

140

HB

20%CT,15%PTFE reinforced, wear-resistant

C106PT1

1.46

0.2-0.3

105

3

8500

100

136

HB

30%GF,5%PTFE reinforced, wear-resistant

C166PT3

1.43

0.2-0.3

150

2

15000

60

140

HB

30%CT,15%PTFE reinforced, wear-resistant