Toughening PP |
MFR |
Density |
Shrinkage |
Tensile Strength at break |
Elongation at break |
Flexural Strength |
Flexural Modulus |
Izod notched Impact Strength |
HDT |
Flame rating |
Characteristic |
|
Test Method |
D1238 |
g/cm3 |
% |
MPa |
% |
MPa |
MPa |
J/m |
℃（1.82MPa） |
1.6mm |
|
|
g/10min |
D792 |
D955 |
D638 |
D638 |
D790 |
D790 |
D256 |
D648 |
UL94 |
||
|
P500 |
2~4 |
0.9 |
1.5-2.0 |
24 |
>200 |
28 |
1100 |
150 |
95 |
HB |
general toughening PP |
|
P580 |
2~4 |
0.9 |
1.5-1.9 |
20 |
>200 |
25 |
1000 |
400 |
80 |
HB |
super tougheningPP |
|
P284 |
2~4 |
1.05 |
1.0-1.2 |
23 |
>25 |
33 |
2200 |
120 |
105 |
HB |
20%Talc filling, toughening |
|
P184CC |
6~8 |
1.04 |
0.6-0.8 |
70 |
4 |
110 |
4200 |
100 |
160 |
HB |
20%Chemically modified GF,toughened |
|
P186CC |
6~10 |
1.13 |
0.5-0.7 |
80 |
4 |
115 |
5500 |
160 |
160 |
HB |
30%Chemically modified GF,toughened |
|
P288 |
8~12 |
1.24 |
0.7-0.9 |
28 |
>10 |
50 |
3100 |
80 |
130 |
HB |
40%Talc filling, toughening |
|
P188CC |
6~10 |
1.22 |
0.3-0.6 |
90 |
4 |
140 |
6500 |
170 |
160 |
HB |
40%Chemically modified GF,toughened |
Used Materials：PP-HI
Hunt Grade：P188CC
Product Feature：High toughness, high strength, easy to shape.